Isolation and/or removal of ionic contaminants from planarization fluid compositions using macrocyclic polyethers

ABSTRACT

The present invention provides fluid compositions for use in the planarization of a substrate surface. Fluid compositions include a planarization slurry having an abrasive component and a chemically interactive component and an effective amount of at least one crown ether that is capable of isolating at least one charged ion contaminant specie in the planarization slurry. Also included are fluid compositions that are pre-treated with an effective amount of at least one crown ether to remove one or more charged ion contaminants in the fluid composition utilized in a planarization process. Methods of using the fluid compositions are also provided.

This is a division of application Ser. No. 09/146,299, filed Sep. 3,1998, (pending), which is incorporated herein by reference.

FIELD OF THE INVENTION

The present invention directed to the isolation of ionic contaminants inplanarization fluid compositions and/or removal of ionic contaminants,such as metallic cations, from planarization fluid compositions, e.g.,slurries, and methods for using such compositions. More particularly,the present invention is directed to planarization fluid compositionsexposed to, i.e., pre-treated, or containing one or more macrocyclicpolyethers or “crown” ethers that selectively chelate ions of a specificsize.

BACKGROUND OF THE INVENTION

A large fraction of yield losses in wafer fabrication or processing ofsemiconductor devices is attributed to contamination. Contaminants canbe organic or inorganic particles, films or molecular compounds, ionicmaterials or atomic species. Examples of ionic contaminants are sodium,potassium, lithium, calcium, boron, manganese, sodium, titanium,zirconium, aluminum, sulfur and magnesium. Other damaging elementalimpurities include heavy metals, for example, such as iron, copper,nickel and gold.

Particularly problematic, however, are analytes, such as high valencemetallic ions, e.g., zirconium (Zr⁺⁴), found in planarization fluidcompositions and used during planarization of wafers. Although suchfluid compositions are generally quite pure, they are, however, not freeof contaminants such as the ionic contaminants listed above. Theseanalytes can destabilize a planarization composition in even minuteconcentrations (ppm or ppb level). The destabilization of the slurryfrom the presence of these analytes can result in aggregate particleshaving sufficient size and mass to cause wafer defects, e.g., scratches.

During planarization, typically a rotating substrate of semiconductormaterial is held against a wetted planarization or polishing surfaceusing a liquid slurry (e.g., a colloidal suspension of abrasiveparticles) under controlled pressure and temperature conditions. Thefluid typically includes an abrasive component, such as alumina, silica,or similar particulates, although, alternatively, a pad could includethe abrasive component. During planarization, abrasive particles andcontaminants such as high valence ions are generally present at thesurface of the substrate being planarized.

Planarization is used to produce a surface with a desired thicknessand/or uniformity. However, typical slurries used in the planarizationprocess contain certain levels of metal ions, particularly high valencemetal ions. Further, such metal ions, particularly high valence metalions, destabilize the colloidal suspension of abrasive particles leadingto aggregation of such abrasive particles. Such aggregation leads towafer detects, e.g., scratches, during the planarization of wafers.

The presence of such metal contaminants during wafer processing hasbecome particularly problematic in high density, integrated circuittechnology. For example, wafer defects caused by contaminants can causea device to fail because of improperly defined patterns caused by thedefects, by creating unpredictable surface topography, by inducingjeakage currents through insulating layers, or by accelerating devicewearout.

It has been reported that certain chelating agents have been added tocleaning solutions commonly used to remove particles and organiccontaminants on silicon surfaces. Such chelating agents tend to reducecertain metallic contamination deposition on a silicon wafer. However,such wet cleaning procedures are performed after CMP processing and ioncontamination and wafer defects such as caused by abrasive particleaggregation may have already caused significant problems to the waferduring the planarization process.

Also, it has been demonstrated that water soluble multidentate chelatingagents, particularly water soluble bidentate ionic chelating agents,such as 1,2-ethylenediphosphonic acid (EDP,), can be used duringplanarization processing to remove metal ion contaminants, as disclosedin U.S. patent application Ser. No. 08/682,308, filed on Jul. 17, 1996,entitled “A Planarization Fluid Composition Including Chelating Agentsand Planarization Method Using Same.”

Thus, improvements in the fluid compositions employed in planarizationprocesses are needed to reduce wafer defects. The present invention, asdescribed below, provides such improvements and overcomes the problemsdescribed above and those problems that will become apparent to oneskilled in the art from the detailed description below.

SUMMARY OF THE INVENTION

The present invention provides fluid compositions for use in theplanarization of a substrate surface, such as a wafer. The fluidcompositions include a planarization slurry that has an abrasivecomponent and a chemically interactive component that interacts with thesurface of the wafer during planarization. The fluid compositions alsoinclude an effective amount of at least one crown ether that is capableof isolating at least one charged ion contaminant specie in theplanarization slurry.

Charged ion contaminant species that can be isolated using the fluidcompositions of the invention include, but are not limited to, ionshaving valences of +2, +3, +4 or more. Preferably, the charged ioncontaminant is a Zr⁺⁴ ion. Typically, the crown ethers employed in theinvention to isolate one or more charged ion contaminants are of theformula benzo or dibenzo-3n-crown-n, where n is a positive wholeinteger. However, other crown ethers known in the art are also useful inthe invention.

Preferably, the fluid composition employed to planarize the surface of awafer, contains a planarization slurry that has an abrasive componentand a chemically interactive component and an effective amount of atleast one crown ether, such as dibenzo-14-crown-4 ether,benzo-15-crown-5 ether, dibenzo-18-crown-6 ether or benzo-21-crown-7ether or a combination thereof. The crown ether or combination thereofis utilized to isolate at least one ion contaminant specie in theplanarization slurry.

A planarization method of the present invention includes providing awafer and a pad that has contact with the wafer surface, thenplanarizing the wafer surface using the pad and a fluid composition. Thefluid composition contains a planarization slurry that has an abrasivecomponent, a chemically interactive component, and an effective amountof at least one crown ether that is capable of isolating at least onecharged ion contaminant specie in the planarization slurry.

The fluid composition used in the planarization method is capable ofremoving or isolating charged ion contaminant species and include, butare not limited to, ions having valences of +2, +3, +4 or more.Preferably, the charged ion contaminant is a Zr⁺⁴ ion. Typically, thecrown ethers employed in the method can isolate and/or remove one ormore charged ion contaminants and are of the formula benzo ordibenzo-3n-crown-n, where n is a positive whole integer. However, othercrown ethers known in the art are also useful in the method.

Also provided, is a method for removing charged ion contaminant speciesfrom a planarization slurry, and includes combining an aqueousplanarization slurry with at least one crown ether in an organic solventto form a mixture. At least one charged ion contaminant specie can thenbe isolated from the slurry by separating the organic solvent layer fromthe aqueous layer to yield a planarization slurry that has a reducedconcentration of the at least one charged ion contaminant specie.

The present invention also provides an isolation method. The methodincludes forming a shallow trench isolation structure that has an oxidesurface and a planarization stop layer formed of silicon nitride. Theoxide surface is planarized using a fluid composition that contains aplanarization slurry that has an abrasive component and a chemicallyinteractive component. The fluid composition also contains an effectiveamount of at least one crown ether that is capable of isolating at leastone charged ion contaminant specie.

In a preferred isolation method, the fluid composition, which containsan abrasive component and a chemically interactive component, has a Zr⁺⁴content of less than 1 ppm, and the planarization process is effectivelystopped on a stop layer formed of silicon nitride.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A and 1B are cross-sectional illustrations of a part of a waferbefore and after a planarization process has been performed inaccordance with the present invention;

FIG. 2 is a general diagrammatical illustration of a chemical-mechanicalpolishing or planarization apparatus utilized in accordance with thepresent invention;

FIG. 3 is an enlarged view of a portion of the dashed circle area ofFIG. 2.

FIGS. 4A-4C are general diagrammatical illustrations showing use of thepresent invention in a shallow trench isolation process.

FIG. 5 is a block diagram of the preparation, i.e., pre-treatment of aplanarization slurry employing a crown ether or a combination of crownethers in an organic solvent layer.

DETAILED DESCRIPTION

The present invention is directed to the selective isolation ofcontaminating analytes, such as high valence ions, in planarizationfluid compositions, e.g., mechanical polishing or planarizationslurries, and/or removal of such contaminating analytes form suchplanarization fluid compositions. The fluid compositions are used inwafer planarization processes. For example, a surface of a structureformed during shallow trench isolation (STI) may be planarized usingsuch a composition. The present invention further provides methods ofplanarization wherein the planarization composition used in aplanarization process has a reduced level of charged ion contaminants,and in particular, high valence charged metal ions such as zirconium(Zr⁺⁴).

Definitions

As used herein, an “effective amount” of a crown ether is a quantitycapable of isolating one or more particular types of contaminatingcharged ions in a composition employed in a planarization method orprocess and/or reducing the concentration of or removing one or moreparticular type of contaminating charged ions, such as metal ions, froma composition employed in a planarization method or process.

As used herein, the term “essentially free” is meant to indicate thatsolvents and/or organic or aqueous layers, i.e., an organic layercomprising a crown ether, employed in preparing fluid planarizationcompositions or slurries of the invention, have less than 20%contaminating ionic species present in the solvent or layer, preferablyless than 10%, and most preferably less than 5% when compared to anon-treated solvent or layer. The term also refers to a treatedplanarization composition or slurry of the invention, i.e., treated byexposure to one or more crown ethers, that has less than 20%contaminating ionic species present in the composition or slurry,preferably less than 10%, and most preferably less than 5% when comparedto a non-treated slurry.

It is further to be understood that the term “planarization” as usedherein is meant to encompass a wide variety of planarization techniques,as well known to one skilled in the art, whereby planarization of asurface is accomplished through mechanical abrasion thereof.Planarization may encompass a chemically active component, such as in,for example, chemical mechanical planarization (CMP). Planarization andpolishing are described generally herein as planarization, as both termsare meant to encompass mechanical abrasion of the surface, even thoughpolishing typically refers to less abrasion than planarization.

As used in this application, “substrate assembly” refers to either asemiconductor substrate such as the base semiconductor layer, e.g., thelowest layer of silicon material in a wafer, or a silicon layerdeposited on another material, such as silicon on sapphire, or asemiconductor substrate having one or more layers or structures formedthereon or regions formed therein. When reference is made to a substrateassembly in the following description, various process steps may havebeen previously used to form or define regions, junctions, variousstructures or features, and openings such as vias, contact openings,high aspect ratio openings, etc.

Planarization Fluid Compositions

Planarization fluid compositions, e.g., slurries, of the presentinvention can be used to reduce the effect of charged ion contaminantspecies, for example, metal and metalloid ions, on abrasive componentsof the fluid composition in a planarization process. By using the fluidcompositions and methods of the present invention, planarization can beeffectively performed without agglomeration of abrasive components whichmay lead to wafer defects. For example, in semiconductor-based devicefabrication, such methods and fluid compositions enable higher yields tobe realized in the fabrication of semiconductor-based integratedcircuits due to the reduction in wafer defects, which often degradeelectrical performance of an integrated circuit.

A typical planarization fluid composition of the invention, comprises anabrasive component that includes abrasive particles and a chemicallyinteractive component as further described herein. Charged ioncontaminants, particularly high valence metal ion species, are generallypresent in these planarization fluid compositions. For example, slurriessuch as Corundum-A and Corundum-B, available from Rodel Inc., Newark,Del., include a substantial quantity of, for example, Zr⁺⁴. Thesecharged ion contaminants destabilize the colloidal suspension ofabrasive particles of the planarization composition and promoteaggregations that can cause defects upon a wafer surface. Aggregationsin planarization fluid compositions are the result of polar interactionsbetween colloidal abrasive particles induced by the charged specieswhich are present in the solution. The critical concentration of chargedions at which these aggregations occur decreases with valence as 1/z⁶,where z is valence of the charged species. This relationship isdescribed by the Shulze-Hardy rule. Because of this 1/z⁶ dependence,high valence ions such as zirconium, Zr⁴⁺, are particularly problematic.Thus, employing one or more crown ethers in a planarization fluidcomposition can be used to effectively isolate problematic charged ioncontaminants, particularly high valence ion species, that are criticalin controlling wafer defects, during a planarization process. Further,employing one or more crown ethers in a planarization fluid compositioncan be used to effectively remove charged ion contaminants, particularlyhigh valence ion species, from a planarization fluid composition priorto use of the composition in planarization.

In addition, to preventing abrasive particle agglomeration, ioncontamination (e.g., metal ion contamination) of wafers can be reducedby employing the present invention. For example, metal ions in theslurries which may bulk diffuse into a surface of a wafer may bereduced. Alternatively, metal ions which may diffuse down fracture pathsof the wafer may be reduced.

Crown Ether Containing Planarization Fluid Composition

Crown ethers are a family of chemical compounds that have the uniqueability to bind with and electrically isolate charged ions. As shown bycompounds I and II below, crown ethers typically consist of a ring ofrepeating (—C—C—O) units. The oxygen atoms are located at the interiorcorners of the ring facets. Each of the oxygen atoms contains two lonepair of electrons that are directed toward the center of the ring likespokes on a wheel creating an electron-rich zone in the center of thering. Positively charged ions that are of suitable size are attracted tothe center of the ring and trapped. By varying the number of repeating(—C—C—O) units, the size of the ring can be adjusted to complex or “fit”specific ions.

The stability of these complexes are found to depend on the number andgeometrical disposition of the ether oxygen atoms and in particular onthe size and shape of potential coordination polyhedra relative to thesize of the cation. Typical examples of crown ethers are given in Table2 as further described below, wherein the numerical prefix indicates thenumber of atoms in the heterocycle and the suffix the number of etheroxygens. The aromatic rings can be substituted, replaced by naphthaleneresidues, or reduced to cyclohexyl derivatives. The “hole size” forcoordination depends on the number of atoms in the ring and is comparedwith conventional ionic radii (readily converted to ionic diameters) asshown in Table 1 below.

Crown ethers useful in the invention can be customized to selectivelychelate ions of a specific size, or if desired, remove them entirelyfrom the slurry as described further below. Crown ethers provide anelectron-rich zone or area in the center of a ring structure, as shownbelow, that can chelate ions, such as metallic ions, of a specific sizeand charge. Thus, depending on the ion to be removed or isolated, acrown ether can be selected or prepared by sizing the crown ether tomatch a specific ion. Crown ethers, are typified by the formulas shownby compound I and II, however, crown ethers with as many as ten oxygensare known and several are commercially available.

In general, and as illustrated by compounds I and II, the formula“3n-crown-n” may be applied to prepare or select different size crownethers. Typically, n≧5, and can be varied to change the size of the ringto match a specific ion to be isolated or removed from a fluidcomposition of the invention. Although this formula is useful as aguide, one skilled in the art will recognize that notable exceptions tothis formula exist, for example, dibenzo-14-crown-4.

As systematic names for crown ethers are very unwieldy, a specialnomenclature is used in which compound I and compound II are called,respectively, 15-crown-5 and dibenzo-18-crown-6. Crown ethers are veryversatile and can be sized to selectively bind with specific ionicspecies. Other known chelation techniques are not so specific. Theelectron-rich area within a crown ether can also effectively isolate theion and stabilize the slurry against the aggregations that can causewafer defects.

The target ion species of which the present invention is beneficial inisolating, reducing, or removing, include but are not limited to, forexample: the alkali metals such as sodium (Na), potassium (K) andLithium (Li); alkaline earth metals such as magnesium (Mg) and calcium(Ca); heavy metals such as iron (Fe), nickel (Ni), and zinc (Zn); andany other metal ion contaminants including, for example, aluminum (Al),chromium (Cr), manganese (Mn), titanium (Ti), boron (B), zirconium (Zr),and copper (Cu); and any other metallic ion or ionic contaminant thatwould form a ligand forming complex with a crown ether of the invention.

A crown ether suitable in the invention is any crown ether soluble in anaromatic hydrocarbon, such as benzene, or other suitable organicsolvent. Preferably, a pre-selected crown ether or combination of crownethers are sized so as to reduce or isolate the amount of high valencemetal ions, such as those that are known or suspected of destabilizingthe colloidal suspension in the planarization fluid composition.Preferably, high valence ion species that can be targeted for isolationor removal in the present invention include all ions having a valence of+2, +3 or +4, such as those shown in Table 1, i.e., +2 ions include Ca,Cu, Fe, Be, Sr, Ba, Ra, Zn, Cd and Hg; +3 ions include Bi, Al, Sc, Y,La, Ga, In, TI, Fe and Cr; +4 ions include C, Si, Ti, Zr, Ce, Ge, Sn andPb. More preferably, the crown ether or combination thereof, is ofsufficient size to remove +4 valence ion species, as such ions are mostlikely to cause agglomeration in planarization compositions. Even morepreferably, the crown ether or ethers are of sufficient size to removeor isolate zirconium (Zr⁺⁴) ions from a fluid composition yielding afluid composition having a (Zr⁺⁴) ion concentration in the range ofabout 100 parts per million (ppm) to about 1 part per billion (ppb),preferably about 1 ppm to about 10 ppb.

A specific crown ether or combination thereof may be selected, forexample, by calculating the ionic diameter of the ion or ions to beremoved or isolated, and selecting one or more crown ethers capable ofcomplexing the ion. For example, Table 1 shows the radii for a varietyof potentially contaminating ions in a fluid composition of theinvention.

TABLE 1 Goldschmidt (G), ^(a)Pauling (P)^(a), and Ladd (L)^(a,b) IonicRadii (Å) Ion G P L Ion G P L H⁻ 1.54 2.08 1.39 Pb²⁺ 1.17 1.21 — F⁻ 1.331.36 1.19 Cl⁻ 1.81 1.81 1.70 Mn²⁺ 0.91 0.80 0.93 Br⁻ 1.96 1.95 1.87 Fe²⁺0.83 0.76 0.90 I⁻ 2.20 2.16 2.12 Co²⁺ 0.82 0.74 0.88 Ni²⁺ 0.68 0.69 —O²⁻ 1.32 1.40 1.25 Cu²⁺ 0.72 — — S²⁻ 1.74 1.84 1.70 Se²⁻ 1.91 1.98 1.81Bi³⁺ 0.2 0.20 — Te²⁻ 2.11 2.21 1.97 Al³⁺ 0.45 0.50 — Sc³⁺ 0.68 0.81 —Li⁺ 0.78 0.60 0.86 Y³⁺ 0.90 0.93 — Na⁺ 0.98 0.95 1.12 La³⁺ 1.04 1.15 —K⁺ 1.33 1.33 1.44 Ga³⁺ 0.60 0.62 — Rb⁺ 1.49 1.48 1.58 In³⁺ 0.81 0.81 —Cs⁺ 1.65 1.69 1.84 Tl³⁺ 0.91 0.95 — Cu⁺ 0.95 0.96 — Ag⁺ 1.13 1.26 1.27Fe³⁺ 0.53 — — Au⁺ — 1.37 — Cr³⁺ 0.53 — — Tl⁺ 1.49 1.40 1.54 NH₄ ⁺ — 1.481.66 C⁴⁺ 0.15 0.15 — Si⁴⁺ 0.38 0.41 — Be²⁺ 0.34 0.31 — Ti⁴⁺ 0.60 0.68 —Mg²⁺ 0.78 0.65 0.87 Zr⁴⁺ 0.77 0.80 — Ca²⁺ 1.06 0.99 1.18 Ce⁴⁺ 0.87 1.01— Sr²⁺ 1.27 1.13 1.32 Ge⁴⁺ 0.54 0.53 — Ba²⁺ 1.43 1.35 1.49 Sn⁴⁺ 0.710.71 — Ra²⁺ — 1.40 1.57 Pb⁴⁺ 0.81 0.84 — Zn²⁺ 0.69 0.74 — Cd²⁺ 1.03 .971.14 Hg²⁺ 0.93 1.10 —

Once the diameter of a particular ion has been established, a crownether having an appropriate or approximate “hole size” can be selectedor prepared. Table 2 provides a comparison of some ionic diameters andcrown ether “hole sizes.”

TABLE 2 Comparison of ionic diameters and crown ether “hole sizes”Cation Ionic Diameter/pm Polyether ring “Hole size”/pm Li¹ 15214-crown-4 120-150 Na¹ 204 15-crown-5 170-220 K¹ 276 18-crown-6 260-320Rb¹ 304 21-crown-7 340-430 Cs¹ 334 — —

In a preferred embodiment, a Zr⁺⁴ ion, based on ionic radii, can beexpected to have an ionic diameter of between about 140-200 pm. Thus, acrown ether, such as dibenzo-14-crown-4 and/or benzo-15-crown-5, may beemployed to isolate or remove Zr⁺⁴ ions. However, other larger crownethers, such as 18-crown-6 and 21-crown-7, may clearly also beeffective.

Charged ion concentration reduction with respect to more than one typeor species of metal ion by employing one or more crown ethers may beaccomplished. However, the reduction of just one metal ion species byone crown ether is beneficial. Furthermore, although it is preferable toobtain a high percentage reduction for at least one metal or one metalspecies, even the slightest reduction of uncomplexed metal ions isbeneficial.

The amount of a crown ether used in a planarization fluid composition ofthe invention is of an effective amount to reduce the concentration ofundesirable metal ions in the fluid composition without impeding thepolishing or planarization rate. Preferably, the crown ether is presentin an amount of about 20 ppb to about 50,000 ppb to an amount less thanabout 0.5% by weight, more preferably to an amount less than about 0.1%by weight based upon the total weight of the fluid composition.

The Planarization Process

FIG. 1A illustrates a portion of a wafer 10 prior to planarization bychemical-mechanical polishing (CMP) in accordance with the presentinvention. The wafer portion 10 includes a substrate 26 having junctions20 formed thereon. Isolation areas 24 are also formed on substrate 26with polysilicon 22 deposited thereon. Over these elements formed onsubstrate 26, a film of borophosphosilicate glass.(BPSG) 12 is formed,and, such as by reflow, the glass 12 conformably covers steps, fillsgaps between polysilicon lines, and forms an upper surface havingdifferent heights such as at areas 14, 16, and 18. The nonplanar uppersurface 13 of BPSG film 12 is the surface having non-uniformities whichcan be reduced or eliminated when subjected to planarization inaccordance with the present invention.

FIG. 1A is shown only to illustrate a surface having nonuniformities inneed of planarization for the fabrication of semiconductor devices.Other surfaces, including but not limited to other dielectrics,polysilicon, oxide filled trenches, such as those employing CVD-SiO₂shallow trench isolation (STI), various metal films, other doped oxides,spin on glasses, or any other fabricated surface which may requireplanarization as is known to one skilled in the art may benefit from thepresent invention. Therefore, the present invention is not limited tothe planarization of any particular surface, but is limited only inaccordance with the invention as described in the accompanying claims.

FIG. 1B illustrates the wafer portion 10 shown in FIG. 1A after theupper surface 13 of the BPSG film 12; has been planarized in accordancewith the present invention. The resulting wafer 10 includes an uppersurface 28 planarized or polished such that the thickness of the wafer10 is substantially uniform across the entire wafer 10 and free ofdefects, e.g., scratches. As will be described further below, thepresent invention provides for a uniformly thick wafer having a reducednumber of wafer defects and reduced metal ion contamination.

The present invention is not limited to use with nonplanar surfaces,such as that shown in FIG. 1A. The present invention is also beneficialfor use with substantially planar surfaces such as the surface 28 shownin FIG. 1B. For example, the slurry and method of planarization inaccordance with the present invention is beneficial during the wholeplanarization process. As such, the benefits are applicable to bothnonplanar and planar surfaces and furthermore through the entireplanarization process.

FIG. 2 is a diagrammatical illustration showing one embodiment of a CMPprocess for planarization of surfaces of semiconductor wafers inaccordance with the present invention. As shown in FIG. 2, the presentinvention utilizes a planarization assembly 29 such as Model 372 orModel 472 available from IPEC/Westech. Other planarization assemblies orunits for performing planarization methods are readily available and areclearly contemplated by the scope of the present invention as describedin the accompanying claims. For example, the planarization process maybe performed with the apparatus described in U.S. Pat. No. 5,421,729,entitled “Apparatus For Planarizing Semiconductor Wafers, and aPolishing Pad for a Planarization Apparatus” and herein incorporated byreference; U.S. Pat. No. 4,193,226 entitled “Polishing Apparatus” andherein incorporated by reference; U.S. Pat. No. 4,811,522 entitled“Counterbalanced Polishing Apparatus” and herein incorporated byreference; and any other planarization assembly as known to thoseskilled in the art. Various other embodiments of planarizationassemblies are known and available for use with the present invention.For example, some planarization units do not use rotating platens androtating wafer holders. The present invention is inclusive of allplanarization units for which the present invention provides benefit.

The general illustrative planarization assembly, as shown in FIG. 2, forperforming planarization in accordance with the present invention,includes a rotating wafer holder 30 that holds wafer 32 of which waferportion 10 is a part thereof. A fluid composition 34 in accordance withthe present invention is introduced on a polishing pad 38. The polishingpad 38 is located on a rotating table platen 36. The polishing pad 38 isapplied to the surface 12 of wafer 10 in the presence of the fluidcomposition 34 at a certain pressure to perform the planarization as isshown in the detail drawing of FIG. 3. The pressure applied isrepresented in FIG. 2 by the arrow mark “P”; this pressure P representsboth down force pressure and backside pressure applied per aplanarization assembly, such as an assembly available from IPEC/Westech.The rotating elements 30, 36 are rotated and moved by motors or drivemeans (not shown) as is readily known to those skilled in the art.

Wafer holder 30 rotates wafer 32 at a selected velocity about an axis 33and moves wafer 32 under controlled pressure P across pad 38. The wafer32 contacts the pad 38 as it is moved. The area of the pad 38 whichcomes into contact with the surface 12 of the wafer 32 varies as thewafer 32 is moved in a predetermined pattern as is known to thoseskilled in the art.

A chemical supply system (not shown) introduces a fluid composition 34atop the pad 38 at a specified flow rate. The fluid composition 34 maybe introduced at various locations about the pad without affecting thebenefits of the present invention. For example, the fluid composition 34may be introduced from above the pad 38, such as by drip, spray, orother dispensing means and further may be introduced from beside therotating table 36 by spraying or other dispensing means.

The rotating table 36 is rotated at a selected velocity and is rotatedin the same direction as the wafer holder 30. The surface 12 of thewafer 32 is held in juxtaposition relative to the pad 38 so that the pad38 can planarize or polish surface 12. The fluid composition and the padpressure primarily determine the polishing rate or rate of removal ofthe surface material.

The benefits of using a fluid composition comprising a crown ether arenot affected by the type or material of the polishing pad utilized. Forexample, the fluid composition may be utilized with any known andappropriate polishing pad as would be known to one skilled in the artbecause the choice of pads is application dependant. For example,suitable pads may include pads such as Model No. IC 1000, Model No. IC60 and Polytech pads, all available from Rodel, Inc., Newark, Del. Thepolishing pad may include one or more pads; may be of specific shape,i.e. circular, oval, or rectangular; may be of a nonuniform shape; andmay be of any particular hardness depending on the particularapplication. Further, as described above, the pads may be pads thatinclude an abrasive component at a surface thereof for planarization.

To alleviate agglomeration of abrasive during the planarization process,the present invention may perform the planarization process in thepresence of a planarization fluid composition (e.g., slurry) 34containing one or more crown ether to isolate one or more species ofcharged ion contaminants. Alternatively, as further described below, aplanarized fluid composition can be pre-treated with one or more crownethers to remove one or more charged ion contaminants suspected to be orknown to be present in the fluid composition.

The planarization fluid composition 34 may generally include an abrasivecomponent and a component that chemically interacts with the surface 12.For example, a typical oxide polishing slurry may consist of a colloidalsuspension of oxide particles, with an average size of, for example 120nm, in an alkali solution having a pH greater than or equal to 9. Ceria(CeO₂) suspensions may also be used when appropriate, particularly wherelarge amounts of SiO₂ must be removed. Ceria acts as both the chemicaland mechanical agent in the slurry. Other abrasive components of theslurry component may include, but are not limited to, alumina (Al₃O₂),silica, zirconium oxide (ZrO₂), titania (TiO₂), or any other abrasiveused in conventional planarization slurries as is known to one skilledin the art. Several slurry solutions presently available, include:Corundum-A (Rodel Inc., Newark, Del.), Corundum-B (Rodel Inc., Newark,Del.), Granite 14, ILD1300 (i.e., an aqueous fumed silica slurryincluding amorphous silica and ammonium hydroxide, available from Rodel,Inc., Newark, Del.) and SC-1 (i.e., a colloidal fumed silica aqueousslurry including amorphous silicon dioxide, DI water, and potassiumhydroxide, available from Cabot Corp. Tuscola, Ill. under the tradedesignation CAB-O-SPERSE SC-1).

General characteristics of suitable conventional slurry componentsutilized in conjunction with the present invention include that thehardness of the polishing particles or abrasive component should beabout the same hardness as the hardness of the film being polished toavoid damaging the film. In addition, the particles should be uniformand the solution free of metallic contaminants. Further, for example,conventional planarization slurries having a pH greater than about 9 areused for oxide polishing processes and those less than a pH of about 4are used in polishing processes of, for example, tungsten. Theconventional slurry used is dependant upon the type of surface beingpolished.

The amount of a crown ether employed in a planarization fluidcomposition and used during planarization according to the presentinvention is an effective amount necessary to reduce the effect of, forexample, particular charged ion contaminants in the fluid compositionsand surfaces with which the fluid compositions are in contact.Concentrations of a particular crown ether or crown ethers used in aplanarization fluid composition of the invention can constitute about1-70% of the fluid compositions in which they are used. Preferably, acrown ether is present in the composition in an amount of less thanabout 50% by weight. More preferably, the crown ether is present in thefluid composition in an amount of less than about 10% by weight.

Preparation of a pre-treated planarization fluid composition that can beemployed in a planarization process of the invention is schematicallyillustrated in FIG. 5. Generally, a planarization slurry 51 suspected orknown to contain charged ion contaminants, particularly unwantedcontaminating high valence ions, can be pre-treated with one or morecrown ethers. Depending on the ion or ions to be removed from theslurry, a preparation of suitable crown ethers in a suitable organicsolvent 52 can be prepared and mixed in a suitable container 53 with theplanarization slurry such that the mixture can be agitated. Bysubsequent settling and separation steps 54, a “cleaned” aqueousplanarization slurry 55 can be obtained and a separate organic layercontaining the crown ethers and isolated ions 56 can be removed.Significantly, the crown ether organic layer sequestering thecontaminating high valence ions, can be recycled by separationtechniques 57 known in the art to yield purified crown ethers containedwithin an organic layer 59 and removed high valence ions 58. This crownether containing organic layer 59 can then be re-employed in furtherpurification of other planarization slurries 51, which along with thepurified crown ether containing organic layer 59 is provided back to themixing tank 53. The final cleaned aqueous planarization fluidcomposition 55 may be employed in a planarization method of theinvention.

Planarization in Shallow Trench Isolation

Although local oxidation of silicon (LOCOS) has long been theconventional process for fabricating isolation, and has the advantage ofbeing both relatively inexpensive and capable of providing isolationover wide areas of a chip. LOCOS has several disadvantages, such as theformation of a “bird's beak” that increases the horizontal space of theisolation, reducing the density of devices on a chip.

Because of its more vertical sidewalls and more planar surface, trenchisolation provides significant advantage over LOCOS in the quest forproviding a high density of integrated circuits. Trench isolationschemes are therefore finding increasing use in semiconductorprocessing. However, because of planarization difficulties, trenchisolation is complex and expensive to process.

Trench isolation process complexity is evident from a general briefdescription of the conventional shallow trench isolation (STI) process.First, thick silicon nitride is deposited on a thin silicon dioxide padon the silicon substrate 80. Then, using conventional photolithography,the silicon nitride 81 is patterned as shown in FIG. 4A defining theisolation areas 83 where STI is desired. Next, the substrate 80 isetched, using, for example, a reactive ion etch (RIE) process, to formshallow trenches 85. A thin layer of silicon dioxide is then grown andsilicon dioxide 87 is deposited, filling the shallow trenches andcovering the patterned silicon nitride 81.

As shown in FIG. 4A, the silicon dioxide 87 has a surface that must beplanarized. The planarization process is quite complex because the oxidedeposition is usually conformal, and therefor narrow areas of isolationmay be at a higher level than wide areas of isolation. Additionally,wide areas of isolation polish much more quickly than narrow areas, aproblem known as dishing may occur. Dishing is a problem, first, becauseoxide in these large areas of STI is thinner than in narrow areas, andsecond because in regions having a low density of devices, the siliconnitride polish stop layer 81 over small, isolated active area regionsmay be completely polished off, and then the active area may getpolished down, introducing potential damage to the substrate 80.

However, at least the slurries available from Rodel (Newark, Del.) andsold under the trade designation Corundum A and Corundum B, effectivelystop planarizing when the silicon nitride stop layer is reached.However, such slurries contain a large amount of high valence +4 chargedion contaminants, e.g., Zr⁺⁴, which leads to abrasive particleagglomeration and wafer scratching. To overcome these difficulties,utilization of a fluid composition, such as Corundum A and Corundum B,pre-treated with one or more crown ethers as described with reference toFIG. 5 may be employed. If a combination of fluid compositions are to beemployed, e.g., Corundum A and Corundum B, each fluid composition ispreferably separately pre-treated, as described above and as set forthin FIG. 5, before the fluid compositions are combined. More preferably,Corundum A is pre-treated and then combined with Corundum B, whetherCorundum B is pre-treated or not pre-treated.

Alternatively, a crown ether containing fluid composition may beutilized during the planarization process. A fluid compositionpre-treated with or incorporating one or more crown ethers during aplanarization process, as described above, can effectively eliminatehigh valence ion-contaminants and therefore prevent or reduce theagglomeration of abrasive particles in a planarization slurry asagglomeration of these abrasive particles may pit or scratch either orboth the silicon oxide (SiO₂) 87 or silicon nitride (Si₃N₄) 81 surfaces.As such, by employing the crown ether fluid compositions of the presentinvention, greater control is provided in stopping the planarizationprocess on the silicon nitride Si₃N₄ while preventing such scratching.

The STI structure resulting after the planarization process is shown inFIG. 4C. After the planarization process, the silicon nitride 81 isremoved yielding defined active areas 90 between oxide regions 87.

All publications, patents and patent documents are incorporated byreference herein, as though individually incorporated by reference.Although the invention has been described with particular reference to apreferred embodiment thereof, variations and modifications of thepresent invention can be made within a contemplated scope of thefollowing claims as is readily known to one skilled in the art.

What is claimed is:
 1. A fluid composition for use in planarization of asurface of a wafer, the fluid composition comprising: a planarizationslurry including an abrasive component and a chemically interactivecomponent that interacts with the-surface of the wafer duringplanarization; and an effective amount of at least one crown ethercapable of isolating at least one charged ion contaminant specie in theplanarization slurry, the at least one charged ion. contaminant specieselected from ions having a valence of +3 or more.
 2. The fluidcomposition of claim 1, wherein the at least one crown ether is a benzoor dibenzo-3n-crown-n ether, where n is greater than or equal to
 5. 3.The fluid composition of claim 1, wherein the at least one charged ioncontaminant specie comprises any metallic ion or ionic contaminant thatproduces a ligand forming complex with the at least one crown ether. 4.The fluid composition of claim 1, wherein the at least one crown etheris soluble in an aromatic hydrocarbon.
 5. The fluid composition of claim1, wherein the at least one charged ion contaminant specie is selectedfrom ions having a valence of +4.
 6. The fluid composition of claim 5,wherein the at least one charged ion contaminant is Zr⁺⁴.
 7. The fluidcomposition of claim 1, wherein the effective amount of the at least onecrown ether in the fluid composition is of an amount less than about0.5% by weight of the total weight of the fluid composition.
 8. Thefluid composition of claim 7, wherein the effective amount of the atleast one crown ether in the fluid composition is of an amount less thanabout 0.1% by weight of the total weight of the fluid composition.
 9. Afluid composition for use in planarization of a surface of a wafer, thefluid composition comprising: a planarization slurry including anabrasive component and a chemically interactive component that interactswith the surface of the wafer during planarization; and an effectiveamount of at least one crown ether capable of isolating at least onecharged ion contaminant specie in the planarization slurry, wherein theat least one crown ether is a benzo or dibenzo-3n-crown-n ether, where nis a positive whole integer.
 10. A fluid composition for use inplanarization of a surface of a wafer, the fluid composition comprising:a planarization slurry including an abrasive component and a chemicallyinteractive component that interacts with the surface of the waferduring planarization; and an effective amount of at least one crownether capable of isolating at least one charged ion contaminant speciein the planarization slurry, wherein the at least one crown ether isdibenzo-14-crown-4 ether, benzo-15-crown-5 ether, dibenzo-18-crown-6ether, or benzo-21-crown-7 ether or a combination thereof.
 11. The fluidcomposition of claim 10, wherein the at least one charged ioncontaminant specie is selected from ions having a valence of +2 or more.12. The fluid composition of claim 11, wherein the at least one chargedion contaminant specie is selected from ions having a valence of +3 ormore.
 13. The fluid composition of claim 12, wherein the at least onecharged ion contaminant specie is selected from ions having a valence of+4.
 14. A fluid composition for use in planarization of a surface of awafer, the fluid composition comprising: a planarization slurryincluding an abrasive component and a chemically interactive componentthat interacts with the surface of the wafer during planarization; andan effective amount of at least one crown ether selected from the groupconsisting of dibenzo-14-crown-4 ether, benzo-15-crown-5 ether,dibenzo-18-crown-6 ether or benzo-21-crown-7ether, wherein the crownether is capable of isolating at least one ion contaminant specie havinga valence of +4 in the planarization slurry.
 15. The fluid compositionof claim 14, wherein the at least one charged ion contaminant is Zr⁺⁴.16. The fluid composition according to claim 14, wherein the effectiveamount of the at least one crown ether in the fluid composition is of anamount less than about 0.5% by weight of the total weight of the fluidcomposition.
 17. The fluid composition according to claim 16, whereinthe effective amount of the at least one crown ether in the fluidcomposition is of an amount less than about 0.1% by weight of the totalweight of the fluid composition.
 18. A planarization fluid compositionfor use during planarization, the fluid composition comprising at leastone crown ether capable of isolating at least one charged ioncontaminant specie in the planarization fluid composition, wherein theat least one charged ion contaminant specie is selected from ions havinga valence of +3 or more.
 19. The fluid composition of claim 18, whereinthe at least one charged ion contaminant specie is selected from ionshaving a valence of +4.
 20. The fluid composition of claim 19, whereinthe at least one charged ion contaminant is Zr⁺⁴.
 21. The fluidcomposition of claim 18, wherein the effective amount of the at leastone crown ether in the fluid composition is of an amount less than about0.5% by weight of the total weight of the fluid composition.
 22. Thefluid composition of claim 21, wherein the effective amount of the atleast one crown ether in the fluid composition is of an amount less thanabout 0.1% by weight of the total weight of the fluid composition.
 23. Aplanarization fluid composition for use during planarization, the fluidcomposition comprising at least one crown ether capable of isolating atleast one charged ion contaminant specie in the planarization fluidcomposition, wherein the at least one crown ether is a benzo ordibenzo-3n-crown-n ether, where n is a positive whole integer.
 24. Thefluid composition of claim 23, wherein n is greater than or equal to 5.25. A planarization fluid composition for use during planarization, thefluid composition comprising at least one crown ether capable ofisolating at least one charged ion contaminant specie in theplanarization fluid composition, wherein the at least one crown ether isat least one of dibenzo-14-crown-4 ether, benzo-15-crown-5 ether,dibenzo-18-crown-6 ether, or benzo-21-crown-7 ether.